Introduction Fiberglass Tissue (Veil)

Fiberglass tissue also called fiberglass veil, mat is made similar as papermaking technology, chopped the continuous glass roving into 6-24mm, mixing and dispersing with water through blender, producing a uniform dense slurry. Then the slurry material is uniform dispersed to a mesh formed fiberglass tiuuse. After dehydration, the fiberglass tissue is going to be treated with binderand sizing agent which imparts the tissue compatible with various media. Finally, the wet binder and sizng agent tissue drought and rolled. The fiberglass tissue is usually produced 30-300g/m2, available width 50mm-2000mm.

Application:

Support for SBS,APP asphalt felt
Fiberglass non-woven roofing tissue is made mineral fiber with excellent anti-corrosion, fire resistance, chemical resistance, great dimension stability, high strength, easy-wet, good compatibility with bitumen. EAS offer RM roofing tissue with reinforced yarn which will greatly improve the tensile and tear strength.

Item	Area weight, g/m2	Binder content, %	Yarn space	Longitudinal tensile Strength N/50mm	Transverse tensile strength N/50mm
RM-50	50	18	/	≥170	≥100
RM-60	60	18	/	≥180	≥120
RM-90	90	20	/	≥350	≥220
RM-100	100	20	/	≥380	≥240
RM-120	120	18	/	≥450	≥300
RM-45R	45	18	15,30	≥200	≥60
RM-50R	50	20	15,30	≥220	≥80
RM-60R	60	20	15,30	≥240	≥100
RM-90R	90	20	15,30	≥400	≥20

timg (1).jpg

Mineral wool acoustic facing or lamination
Fiberglass non woven veil for facing is excellent surface smooth, low fuzz and compatible with various coating. EAS offer high quality and economic facing tissue for mineral wool, rockwool lamination and decoration.

Item	Area weight, g/m2	Binder content, %	Longitudinal Tensile Strength N/50mm	Transverse tensile strength N/50mm
TM-40	40	≤25	≥120	≥60
TM-50	50	≤25	≥150	≥75
TM-100	100	≤25	≥250	≥150

PCB,CEM-3 renforcement
E glass non woven tissue is excellent electric insulation and heat resistance. EAS’s PCM tissue for CEM-3 can meet IPC-4130. It is well compatible with epoxy resin system.

Item	Area weight, g/m2	Binder content, %	Longitudinal tensile Strength N/50mm	Transverse tensile strength N/50mm
PCM-75	75	11	≥225	≥150
PCM-60	105	11	≥240	≥160